Detalle de: Poly(acrylic acid) as an adhesion promoter for UV-assisted thermoplastic bonding: Application for the in vitro construction of human blood vessels

In this study, we introduced a novel adhesion bonding method for fabricating thermoplastic microdevices using poly(acrylic acid) (PAA) as a UV-assisted adhesion promoter. The bonding mechanism was based on the covalent cross-links between poly(methyl methacrylate) (PMMA) and PAA via the free radicals in their carbon backbone generated under UV irradiation. The water contact angle and Fourier-transformed infrared (FTIR) analysis were performed to analyze the surface characteristics of the PAA-coated PMMA. PMMAs were bonded under UV treatment for 60 s with the highest bond strength of around 1.18 MPa. The PMMA microdevice was leak-proof for over 200 h. Besides, clog-free PMMA microdevices with various-sizes microchannels were performed to demonstrate such a high applicable bonding method for microdevice fabrication. Moreover, PMMAs were bonded with other thermoplastics with a bond strength of around 0.5 MPa. Notably, collagen was easily coated inside the PMMA microchannels via electrostatic interaction between PAA and collagen which is beneficial for on-device cell culture. As a result, a layered co-culture model of smooth muscle cells (SMCs) and human umbilical vein endothelial cells (HUVECs) was realized inside simple straight microchannels mimicking human blood vessel wall. Therefore, the introduced bonding method could pave the way for fabricating microdevice for cell-related applications.